| Title: | Chemical and Thermo-Mechanical Properties of Waterborne Polyurethane Dispersion Derived from Jatropha Oil |
| Author(s): | Saalah S; Abdullah LC; Aung MM; Salleh MZ; Awang Biak DR; Basri M; Jusoh ER; Mamat S; Osman Al Edrus SS; |
| Address: | "Chemical Engineering Programme, Faculty of Engineering, Universiti Malaysia Sabah, Jalan UMS, Kota Kinabalu 88400, Sabah, Malaysia. Department of Chemical and Environmental Engineering, Faculty of Engineering, Universiti Putra Malaysia, Serdang 43400, Selangor, Malaysia. Higher Institution Centre of Excellence Wood and Tropical Fibre (HICoE), Institute of Tropical Forestry and Forest Products, Universiti Putra Malaysia, Serdang 43400, Selangor, Malaysia. Department of Chemistry, Faculty of Science and Technology, Universiti Putra Malaysia, Serdang 43400, Selangor, Malaysia. Radiation Processing Technology Division, Malaysian Nuclear Agency, Kajang 43000, Selangor, Malaysia. School of Engineering Technology, Malaysian Institute of Chemical and Bioengineering Technology (UniKL MICET), Universiti Kuala Lumpur, Taboh Naning, Alor Gajah 78000, Melaka, Malaysia" |
| ISSN/ISBN: | 2073-4360 (Electronic) 2073-4360 (Linking) |
| Abstract: | "Nowadays, there is a significant trend away from solvent-based polyurethane systems towards waterborne polyurethane dispersions due to government regulations requiring manufacturers to lower total volatile organic compounds, as well as consumer preference for more environmentally friendly products. In this work, a renewable vegetable oil-based polyol derived from jatropha oil was polymerized with isophorone diisocyanate and dimethylol propionic acid to produce anionic waterborne polyurethane dispersion. Free standing films with up to 62 wt.% bio-based content were successfully produced after evaporation of water from the jatropha oil-based waterborne polyurethane (JPU) dispersion, which indicated good film formation. The chemical and thermo-mechanical properties of the JPU films were characterized. By increasing the OH numbers of polyol from 161 mgKOH/g to 217 mgKOH/g, the crosslinking density of the JPU was significantly increased, which lead to a better storage modulus and improved hydrophobicity. Overall, JPU produced from polyol having OH number of 217 mgKOH/g appears to be a promising product for application as a binder for wood and decorative coatings" |
| Keywords: | crosslinking density jatropha oil water-based coatings waterborne polyurethane dispersion; |
| Notes: | "PubMed-not-MEDLINESaalah, Sariah Abdullah, Luqman Chuah Aung, Min Min Salleh, Mek Zah Awang Biak, Dayang Radiah Basri, Mahiran Jusoh, Emiliana Rose Mamat, Suhaini Osman Al Edrus, Syeed SaifulAzry eng FRGS/1/2017/TK05/UMS/02/2/Ministry of Higher Educations Malaysia/ Switzerland 2021/04/04 Polymers (Basel). 2021 Mar 5; 13(5):795. doi: 10.3390/polym13050795" |